Introduction Alumina ceramic plunger piston
Alumina Ceramic plunger piston work exceptionally well in wear-resistance, high temperature, saltwater, chemical, and metering applications. It has the advantages of super hardness, high wear-resisting, good corrosion resistance resistant acid-base, high intensity, high temperature tolerance, high mechanical strength and so on. It is widely used in various mechancal field.
The Ceramic Plunger For Pump Parts is made of high-purity ceramic raw materials, which are formed by dry pressing or cold isostatic pressing, high-temperature sintering and precision machining.
Ceramic Plunger For Pump Parts can work in the acid and alkali corrosion conditions, high toughness and low friction coefficient, high pressure environment for a long time, and the maximum temperature to 1800 ºC (3272ºF)…
Characteristics Alumina ceramic plunger piston
Shaft plunger | Pump plunger |
Wear Plunger rod | Filling Pump plunger |
Pins rod | Water Pump plunger |
Pump piston rod | Plunger rod |
Pump shaft rod | Sleeve and bushing plunger |
Machinable plunger | Piston plunger |
Tip: For different industries, equipment,and environment, ceramic plunger have different function, We can machining ceramic plunger shaft piston rod , such as surface polishing, internal and external pipe wall threads, metal parts bonded, different shapes etc by custom requirement. |
Technical Data Sheet of Alumina ceramic plunger piston
Item | Test condition | Unit | 96% alumina ceramics | 99% alumina ceramics | 99.5-99.7% alumina ceramics |
Chemical ingredients | Al2O3 | Al2O3 | Al2O3 | ||
Bulk Density | g/cm3 | >3.6 | 3.88 | 3.90 | |
Max. Use Temp. | 1450℃ | 1600℃ | 1650℃ | ||
Water absorption | % | 0 | 0 | 0 | |
ROHS Hardness | ≥85 | ≥89 | ≥89 | ||
Flexural strength | 20℃ | Mpa(psix10^3) | 358(52) | 550 | 550 |
Compressive Strength | 20℃ | Mpa(psix10^3) | 2068(300) | 2600(377) | 2600(377) |
Fracture Toughness | K(l c) | Mpa m^1/2 | – | – | – |
Coefficient of thermal expansion | 25-1000℃ | 1X10^-6/℃ | 7.6 | 7.9 | 8.2 |
Coefficient of thermal conductivity | 20℃ | W/m.K | 16 | 17-30.0 | 17-30.4 |
Thermal Shock Resistance | ^Tc | ℃ | 250 | 200 | 200 |
Dielectricity constant | 1MHz.25℃ | 9 | 9.7 | 9.7 | |
Dielectric strength | ac-kV/mm(ac V/mil) | 8.3(210) | 8.7(220) | 8.7(220) | |
Volume Resistivity | 100℃ | ohm-cm | >10^13 | >10^14 | >10^14 |